Fig 2.

A) Example (n = 1) polymerization profiles of unmixed initiator paste of M₁₀PPG at different temperatures. The paste contains 3 wt% BP and 20 wt% MCPM with no activator nor TSrP. B) Average (n = 1) inhibition time (t_i; circles), R_p,max (diamond), and final monomer conversion (triangle) of M₁₀TEG and M₁₀PPG initiator pastes plotted as Ln(1/t_i) or Ln(R_p,max) versus inverse of temperature (Arrhenius plots). Reaction rates at a given temperature were largely similar for M₁₀TEG compared with M₁₀PPG although delay times and final conversions were significantly and slightly reduced respectively.