Table 2.
Vibrating sample magnetometer measurements.
| LW-ONW | LW-ONW (102.4 kA) | LW-NINW | LW-NINW (102.4 kA) | OBS1 | OBS1 (103.2 kA) | ECF2LAP | ECF2LAP (101.6 kA) | R-1 | R-1 (~25 kA) | R-1 (7.0 kA) | K38-PC2 | K38-PC2 (23.4 kA) | K38-PC2 (7.0 kA) | SHV347-B | SHV347-B (~25 kA) | SHV347-B (7.2 kA) | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Ms (A·m2/kg) | 1.46 | 1.85 | 1.71 | 2.32 | 0.20 | 5.39 | 0.92 | 2.98 | 0.71 | 0.86 | 1.01 | 1.99 | 2.29 | 2.05 | 1.91 | 2.28 | 1.92 |
| Mr (A·m2/kg) | 0.39 | 0.34 | 0.57 | 0.49 | 0.02 | 0.09 | 0.15 | 0.16 | 0.13 | 0.13 | 0.12 | 0.30 | 0.27 | 0.30 | 0.34 | 0.32 | 0.32 |
| Hc (kA/m) | 26.58 | 22.36 | 45.68 | 33.18 | 6.37 | 4.38 | 13.53 | 9.71 | 15.68 | 14.16 | 12.97 | 9.87 | 7.32 | 9.63 | 13.45 | 11.86 | 12.65 |
| R-1 | R-1 (25.4 kA) | R-1 (7.2 kA) | K38-PC2 | K38-PC2 (25.6 kA) | K38-PC2 (6.9 kA) | SHV347-B | SHV347-B (24.9 kA) | SHV347-B (7.0 kA) | |||||||||
| Ms (A·m2/kg) | 0.67 | 1.70 | 2.04 | 1.99 | 2.31 | 2.10 | 1.91 | 2.47 | 2.05 | ||||||||
| Mr (A·m2/kg) | 0.12 | 0.13 | 0.15 | 0.30 | 0.30 | 0.29 | 0.34 | 0.35 | 0.30 | ||||||||
| Hc (kA/m) | 15.28 | 9.71 | 6.45 | 10.27 | 8.28 | 9.71 | 13.29 | 11.86 | 10.58 |
Measurement of all samples in the upper half of the table, with pre-experimental values labeled with just the sample name and post-experimental values labeled with the sample name and the peak current value in parentheses; Repeated measurement of intermediate samples in the lower half of the table to check for pre-experimental consistency and post-experimental variability. Saturation magnetization (Ms), remanent magnetization (Mr), and coercivity (Hc) are shown.