. 2016 Apr 7;8(4):124. doi: 10.3390/polym8040124

Table 2.

Straps tested for their residual strength and stiffness properties after 1, 2, 3 and 11 million load cycles at an upper stress level (σu) of 720–750 MPa. The fibre parallel elastic modulus E11 was calculated from linear encoder measurements (E11_LE). Straps are labelled with B or R, depending on the author who manufactured them, followed by the number of the strap.

Strap σu [MPa] Number of cycles tested σUTS [MPa] σUTS [%] E11_LE [GPa] E11_LE [%]
Average - - 1,620 ± 65 100.0 165.9 ± 4.0 100.0
B11 750 1.00 × 106 1,575 97.2 170.2 102.6
B12 720 1.00 × 106 1,627 100.4 166.6 100.5
B13 750 2.00 × 106 1,618 99.9 - -
B15 750 3.00 × 106 1,725 106.5 166.0 100.1
R70 750 11.09 × 106 1,557 96.1 160.6 96.8