Table 2.

Results of the analyses of thermosets (ATG, DSC, DMA).

Thermoset	Curing agent	Resin type	Td5% (°C)a	Tdmax (°C)a	W% chara	Tg(°C)b	Tα (°C)c	E′glassy (Mpa)c	E′elastic (Mpa)c
1	DA10	GDF10EPO	296	356	9.9	5	x	x	X
2	DA10	GDF14EPO	299	356	7.7	4	x	x	x
3	DA10	GDF16EPO	306	365	8.6	3	x	x	x
4	DIFFA	GDF10EPO	282	368	16.9	15	x	x	x
5	DIFFA	GDF14EPO	286	378	13.6	11	x	x	x
6	DIFFA	GDF16EPO	282	376	15.9	16	x	x	x
7	IPDA	GDF10EPO	310	369	9.0	21	x	x	x
8	IPDA	GDF14EPO	298	352	10.9	23	x	x	x
9	IPDA	GDF16EPO	297	367	10.0	18	x	x	x
10	IPDA	87%-GDF14EPO 13%-GTF-EPO	290	378	10.1	25	x	x	x
11	IPDA	75%-GDF14EPO 25%-GTF-EPO	287	373	9.7	28	x	x	x
12	IPDA	50%-GDF14EPO 50%-GTF-EPO	289	371	14.2	45	61	678	3.5
13	IPDA	25%-GDF14EPO 75%-GTF-EPO	282	372	15.9	54	63	1,985	7.5
14	IPDA	10%-GDF14EPO 90%-GTF-EPO	266	371	18.7	60	71	2,523	9.7
15	IPDA	GFT-EPO	279	372	17.5	62	72	1,685	8.8

^aDetermined by TGA (10°C.min^-1, N₂ flow).

^bDetermined by DSC on the second heat-cool-heat cycle (10°C.min^-1, N₂ flow).

^cDetermined by DMA (frequency 1 Hz, amplitude 7 μm, 3°C.min^-1). E'_glassy at 30°C, E'_elastic at 150°C.