Table 2.

Hardness H_IT, indentation modulus E_IT and fractional content ϕ of tested material constituents.

R	Constituent	µMIT	σMIT	µHIT	σHIT	ϕ
(mm)		(GPa)	(GPa)	(GPa)	(GPa)	(%)
1	1	28.42	4.16	0.74	0.21	50.90
	2	66.13	23.69	8.87	4.98	49.10
3	1	28.05	5.53	0.89	0.26	60.40
	2	74.51	24.12	10.16	4.64	39.60
11	1	33.23	10.17	1.43	0.91	44.10
	2	92.63	7.99	13.02	1.62	55.90
26	1	25.54	5.88	0.99	0.39	52.40
	2	78.44	10.14	11.41	2.66	47.60
34	1	31.12	4.38	1.16	0.36	44.80
	2	69.36	20.21	8.42	5.04	55.20
40	1	25.06	3.04	0.77	0.22	51.50
	2	54.80	19.31	5.23	3.97	48.50
45	1	19.52	3.76	0.49	0.13	78.00
	2	39.42	16.14	2.21	1.15	22.00