. 2019 May 7;11(5):826. doi: 10.3390/polym11050826

Table 2.

Dynamic mechanic and thermal properties of the cured TO-based resins.

Samples	E′₂₅^a (GPa)	T_g^b (°C)	ν_e^c (10³ mol/m³)	T₅^d (°C)	T_p1^e (°C)	T_p2^e (°C)	w_char^f (%)
TOPERMA	2.05	123.1	3.44	384.9	408.0	453.8	9.04
TOPERMA-HEA	2.07	125.8	4.28	380.2	413.0	455.1	8.45
TOPERMA-HEMA	2.11	125.0	3.75	370.8	403.8	442.7	10.2
TOPERMA-MAA	2.33	130.3	3.93	379.5	406.4	452.3	8.36

^a Storage modulus at 25 °C. ^b Glass transition temperature. ^c Crosslink density. ^d 5% weight loss temperature. ^e Peak temperature at the curves of weight loss rate; two peak values were observed for all the samples. ^f Char yield.