Published in final edited form as: Chem Rev. 2019 Mar 27;119(8):5298–5415. doi: 10.1021/acs.chemrev.8b00593

Figure 47.

Figure 47.

(A) Long cycling performance of Li3V2(PO4)3 mesoporous hollow nanofibers for a large number of 9500 cycles in a lithium half-cell. The inset shows a schematic of the lithiation and delithiation processes of mesoporous hollow nanofibers. (B) Three-dimensional view of the mat comprised of aligned carbon nanofibers containing In2O3 nanoparticles before and after electrochemical cycling. (C) The voltage versus specific capacity profiles of fully flexible LIB before and after 30, 60, 90, and 120 cycles of bending. (D) Schematic illustration of the stretchable PVDF@ Ni@Si core−sheath nanofiber-based mat, and (E) the bending cycle performance of the LIB wih the use of the mat as the negative electrode. (A) Reprinted with permission from ref 439. Copyright 2015 Springer Nature. (B and C) Adapted with permission from ref 721. Copyright 2015 Elsevier. (D and E) Adapted with permission from ref 722. Copyright 2014 Royal Society of Chemistry.