Table 1.

Electrochemical performance of various supercapacitors fabricated based on AC/PANI material.

Material Specific Capacitance Capacity Retention
(Cycle Number)
Energy, Power Density
/Wh kg−1, kW kg−1
Ref.
Porous carbon nanosheets/PANI 512 F g−1 at 1 A g−1 91% (3000) 22.3, 14 [26]
Enteromorpha prolifera-derived AC/PANI 622 F g−1 at 1 A g−1 87% (2000) / [27]
Hierarchical porous carbon/PANI 531 F g−1 at 0.5 A g−1 96% (10,000) 17.3, 1.06 [28]
Bamboo carbon/PANI 277 F g−1 at 0.5 A g−1 92% (1000) 47.5, 0.22 [29]
Wood-derived porous carbon/PANI 347 F g−1 at 2 A g−1 67% (2500) 44.4, 3.15 [30]
N-doped porous carbon/PANI fiber 755 F g−1 at 1 A g−1 91% (1000) / [31]
N‑self-doped carbon framework/PANI 373 F g−1 at 1 A g−1 80% (5000) 22.2, 7.31 [32]
AC/PANI 378 F g−1 at 1 A g−1 / / [33]
Cellulose-derived carbon/PANI 3.3 F cm−2 at 1 mA cm−2 83% (3000) / [34]
Cellulose-derived porous carbons/PANI 765 F g−1 at 1 A g−1 91% (5000) / [35]