Table 3.

General tensile properties of electrospun fiber mats of pure PEO, blend PEO/PANI, and side-by-side (SBS) PEO/PANI.

Code		Tensile modulus (MPa)	Stress at 10% strain (MPa)	Stress at 20% strain (MPa)	Elongation at break (%)	Maximum strength (MPa)
PEO 3%	Pure	63.8 ± 8.5	4.9 ± 1.0	7.0 ± 0.6	618 ± 149	14.4 ± 1.5
	3%–1.5% SBS	49.2 ± 3.0	3.7 ± 0.3	5.0 ± 0.3	202 ± 45	5.8 ± 0.3
	3%–2.5% SBS	38.6 ± 2.8	2.7 ± 0.2	3.3 ± 0.5	245 ± 79	4.9 ± 0.8
	3%–3.5% SBS	27.6 ± 6.5	2.2 ± 0.4	3.2 ± 0.6	292 ± 51	4.3 ± 0.6
	3%–2.5% blend	39.8 ± 6.2	2.9 ± 0.2	3.7 ± 0.2	88 ± 14	3.8 ± 0.2
PEO 4%	Pure	113.3 ± 13.2	6.3 ± 0.4	8.0 ± 0.3	490 ± 96	15.4 ± 1.2
	4%–1.5% SBS	91.3 ± 6.6	4.6 ± 0.2	6.5 ± 0.6	364 ± 75	8.3 ± 0.3
	4%–2.5% SBS	71.4 ±4.1	3.3 ± 0.3	4.2 ± 0.3	385 ± 78	6.7 ± 0.5
	4%–3.5% SBS	51.9 ± 6.9	2.7 ± 0.3	3.8 ± 0.3	305 ± 47	5.4 ± 0.4
	4%–2.5% blend	58.7 ± 6.2	4.2 ± 0.4	5.6 ± 0.5	201 ± 19	6.8 ± 0.3
PEO 5%	Pure	121.7 ± 20.8	6.7 ± 0.9	9.6 ± 0.6	604 ± 60	17.8 ± 2.5
	5%–1.5% SBS	86.3 ± 9.2	5.3 ± 0.3	6.1 ± 0.3	751 ± 62	8.2 ± 0.4
	5%12.5% SBS	78.7 ± 6.8	4.2 ± 0.2	5.5 ± 0.3	692 ± 53	7.8 ± 0.2
	5%–3.5% SBS	57.2 ± 7.6	3.8 ± 0.3	4.6 ± 0.4	721 ± 117	7.9 ± 0.6
	5%–2.5% blend	Not Spinnable