. 2018 Nov 6;3(11):14986–15001. doi: 10.1021/acsomega.8b02229

Table 1. Magnetic Moment Obtained at H = 4 T (M_s), Remanent Magnetization (M_r), and Coercivity Field (H_c) Estimated for the CoFe₂O₄, NiFe₂O₄, and Co_0.5Ni_0.5Fe₂O₄ NPs Measured at Four Temperatures.

sample	temp (K)	M_s (emu/g)	M_r (emu/g)	H_c (Oe)	M_r/M_s
CoFe₂O₄	300	52.63	20.87	1274	0.40
	100	57.21	46.499	8862	0.81
	10	56.25	48.367	13 002	0.86
	1.8	56.42	48.367	13 002	0.86
NiFe₂O₄	300	30.21	4.00	159	0.13
	100	33.23	8.58	360	0.26
	10	33.27	10.41	422	0.31
	1.8	33.81	9.92	481	0.29
Co_0.5Ni_0.5Fe₂O₄	300	43.56	15.62	886	0.36
	100	47.81	35.40	6591	0.74
	10	47.40	37.16	8955	0.78
	1.8	47.53	37.16	8955	0.78

Table 1. Magnetic Moment Obtained at H = 4 T (Ms), Remanent Magnetization (Mr), and Coercivity Field (Hc) Estimated for the CoFe2O4, NiFe2O4, and Co0.5Ni0.5Fe2O4 NPs Measured at Four Temperatures.