Table 1. Specific Capacitances of OFG at Different Scan Rates of CV and Current Densities of Galvanostatic Charge/Discharge Experiments Wherein the Electrodes Were Prepared with the PVDF Binder and NMP Was Used for OFG Dispersion^a.

scan rate (mV s^–1)	specific capacitance (F g^–1)	current density (A g^–1)	specific capacitance (F g^–1)
100	197
50	207
20	219	10	213
10	228	5	221
5	237	2	240
2	260	1	272
1	318	0.5	331
retention	62%	retention	64%

Electrodes were dried at 170 °C.