Table 2. Comparison of Electrical Properties of Some Recently Reported ECAs.

	content	curing temperature (°C)	electrical resistivity (10–5 Ω cm)
this work	55 wt % Ag flakes, 3 wt % CNTs and 2 wt % CBs, 40% TPU	180	32.84
Li et al.5	80 wt % Ag flakes, 20 wt % PU	180	1
Yao et al.12	70 wt % KI treated Ag, 30 wt % epoxy resin	150	10.8
Yao et al.32	50 wt % Ag, 4.5 wt % CNTs, 45.5 wt % PU	120	270.27
Zhao et al.40	80 wt % Ag flakes,1.5 wt % sodium dodecyl sulfate-stabilized graphene nanosheets, 18.5% epoxy resin	150	1.6
Zhang et al.18	80 wt % of 4: 6 molar ratio of Ag nanoparticles and Ag flakes, 20 wt % epoxy resin	230	0.6
Zhang et al.41	75 wt % of 2: 3 Ag nanowires and Ag flakes, 25 wt % epoxy resin	300	0.58
Wen et al.34	70 wt % Ag flakes, 2.5 wt % polypyrrole nanoparticles, 27.5 wt % epoxy resin	160	9.4
Wen et al.42	65 wt % Ag flakes, 0.5 wt % polyaniline particles, 34.5 wt % PU	25	14.5