. 2019 Jul 22;11(7):1220. doi: 10.3390/polym11071220

Table 2.

Comparison between the physical properties of as-received and printed PETG.

Material Printing Temperature °C Density (g/cm3) Porosity content * (%) Young’s Modulus (MPa) Tensile Strength
(MPa)
Elongation at Break (%) Fracture Toughness
MPa × m1/2
as-received - 1.26–1.28 0 791 ± 91 54.3 ± 1.3 400 ± 220 2.11–2.54
printed 240 1.03 ± 0.01 19 ± 0.9 491 ± 13 32.3 ± 3.2 8.8 ± 0.2 1.81 ± 0.01
250 1.07 ± 0.02 16 ± 1.6 478 ± 51 34.0 ± 3.3 11.7 ± 2.0 2.09 ± 0.01

* based on density measurements.