Table 1.

Benchmark comparison of low-temperature printed conductive silver traces. “—” indicates that metric was not reported in original work. Values given in italics are approximated from information given in report

Ink Type	Deposition	Substrate	Curing Temp (°C)	Curing Time	Resistivity (Ω cm)	△R/R @ 50% bending strain	△R/R @ 1000 bend cycles	Reference
AgNW	Aerosol Jet	Kapton	80	2 min	6.9*10−5	—	—	this work
AgNW	Aerosol Jet	Kapton	20	2 min	8.4*10−4	1.07	1.15 @ 1.0mm (5% strain)	this work
AgNW	Screenprint	PET/ glass	150	15 min	2.1*10−5	1.13	—	26
AgNP- eInGa	Inkjet	Transfer paper	60	45 min	2.8*10−5	1.48	—	54
Ag micro flakes	3D Print	Artificial skin	20	5 min	7.2*10−3	>1.5	—	37
AgNP	Pen	Paper	25	24 hours	2.0*10−4	—	1.36 @ 1.6mm (1.5% strain)	38
AgNP	3D Print	Kapton	150	24 hours	1.0*10−3	2.95	2 @ 5.0mm (1% strain)	55
AgNP	Inkjet	Kapton	150	1 hour	1.5*10−1	4	1.15 @ 2.5mm (2% strain)	56
Bulk Silver	—	—	—	—	1.6*10−6	—	—	—