Table 6.

OCP curve features for the 18-14, 18-15, and 18-13-1 alloys before and after TMT, and the 18-14-based foam material in Hanks’ solution at 310 K.

Alloy	TMT	E, mV (SSCE)
		E0	Est	ΔE
18-14	Before	−529	−241	288
	After	−241	1	240
18-15	Before	−427	−244	183
	After	−355	−175	180
18-13-1	Before	−131	−48	83
	After	−346	99	445
18-14 (foam)	−	−265	−96	169