Table 10.

The results of OCP curves approximation for the 18-14, 18-15, and 18-13-1 alloys before and after TMT, and the 18-14-based foam material in Hanks’ solution at 310 K.

Alloy	TMT	Period	tx, s	a	k	c	R2
18-14	Before	A	2600	−0.002	0.370	0.003	0.999
		B		2.882	0.206	−1086	0.994
	After	A	700	−0.064	0.156	0.237	0.998
		B		2.831	0199	723	0.996
18-15	Before	A	2900	−0.002	0.232	0.009	0.999
		B		4.030	0.330	586	0.998
	After	A	1800	−0.012	0.383	0.002	0.999
		B		3.901	0.313	−706	0.990
18-13-1	Before	A	800	−0.067	0.225	0.068	0.989
		B		1.281	0.017	−750	0.962
	After	A	600	0.010	0.267	0.010	0.991
		B		2.843	0.207	−587	0.986
18-14 (foam)	−	A	5500	−0.012	0.557	0.001	0.996
		B		3.373	0.262	−3217	0.999