Table 3.

Comparison of the effective atomic number (Z_eff) and electron density (N_el) of the selected glasses obtained using MCNP5 and Geant4 simulation and experimental results.

PbO %	0.356 MeV						0.662 MeV
	Zeff			Nel×1023			Zeff			Nel×1023
	MCNP5	Exp.	Geant4	MCNP5	Exp.	Geant4	MCNP5	Exp.	Geant4	MCNP5	Exp.	Geant4
5	12.40	12.21	12.02	3.15	3.10	3.06	11.74	11.64	11.59	2.99	2.96	2.95
10	12.76	12.44	12.23	3.23	3.15	3.10	11.94	11.76	11.70	3.02	2.98	2.96
15	13.11	12.60	12.44	3.30	3.17	3.13	12.15	11.83	11.81	3.06	2.98	2.97
20	13.46	12.87	12.64	3.37	3.22	3.17	12.35	12.02	11.93	3.10	3.01	2.99
25	13.79	13.05	12.83	3.44	3.25	3.20	12.55	12.12	12.04	3.13	3.02	3.00
30	14.11	13.18	13.01	3.50	3.27	3.23	12.76	12.19	12.15	3.17	3.02	3.01
35	14.43	13.37	13.18	3.56	3.30	3.26	12.96	12.32	12.26	3.20	3.04	3.03
40	14.73	13.56	13.35	3.62	3.33	3.28	13.17	12.45	12.37	3.24	3.06	3.04
45	15.03	13.73	13.52	3.68	3.36	3.30	13.38	12.57	12.48	3.27	3.07	3.05
	1.173 MeV						1.33 MeV
5	11.53	11.42	11.46	2.93	2.90	2.91	11.49	11.39	11.45	2.92	2.90	2.91
10	11.67	11.51	11.53	2.95	2.91	2.92	11.62	11.48	11.53	2.94	2.90	2.92
15	11.81	11.57	11.61	2.97	2.91	2.92	11.76	11.55	11.60	2.96	2.91	2.92
20	11.95	11.67	11.69	2.99	2.93	2.93	11.90	11.64	11.68	2.98	2.92	2.93
25	12.10	11.74	11.76	3.02	2.93	2.93	12.04	11.70	11.75	3.00	2.92	2.93
30	12.24	11.81	11.84	3.04	2.93	2.94	12.18	11.78	11.82	3.02	2.92	2.93
35	12.39	11.91	11.92	3.06	2.94	2.94	12.33	11.87	11.89	3.04	2.93	2.94
40	12.54	12.00	11.99	3.08	2.95	2.95	12.48	11.97	11.97	3.07	2.94	2.94
45	12.70	12.09	12.08	3.10	2.96	2.95	12.63	12.05	12.05	3.09	2.95	2.95