Table 7.

Comparative analysis of starch bioplastics with relative research.

Si. No.	Test/Analysis	Results	Available results		Results Deviation	Remarks
01	Thermal decomposition (50% of weight loss)	291 °C	250 °C	Nurul et al. [28]	41 °C	Increased (16.4%)
02	Melting temperature (Tm)	297 °C	132.3 °C	Seyed et al. [27].	164.8 °C	Increased
03	Glass Transition temperature (Tg)	57.2 °C	21.6 °C	Seyed et al. [27].	35.6 °C	Increased
04	Tensile Strength	3.55 MPa	2.66 MPa	Seyed et al. [27].	0.89 MPa	Increased (33.45 %)
05	Elongation	88.1	86.7	Seyed et al. [27].	1.4	Increased (1.6 %)
06	Surface Roughness (Average)	0.6 μm	26 nm	Romera et al. [38]		Comparative better