Table 8.
Comparative analysis of composite bioplastics with relative research.
| Si. No. | Test/Analysis | Results | Available results | Results Deviation | Remarks | |
|---|---|---|---|---|---|---|
| 01 | Thermal decomposition (50% of weight loss) | 303 °C | 310 °C | Nurul et al. [28] | -7 °C | Decreased (2.25%) |
| 02 | Melting temperature (Tm) | 303 °C | 136.6 °C | Seyed et al. [27]. | 166.4 °C | Increased |
| 03 | Glass Transition temperature (Tg) | 66.8 °C | 35.3 °C | Seyed et al. [27]. | 35.6 °C | Increased |
| 04 | Tensile Strength | 3.95 MPa | 3.56 MPa | Seyed et al. [27]. | 0.39 MPa | Increased (10.95 %) |
| 05 | Elongation | 62.5 | 62.79 | Seyed et al. [27]. | -0.29 | Decreased (0.46 %) |
| 06 | Surface Roughness (Average) | 1 μm | 26 nm | Romera et al. [38] | Comparative better | |