Table 1. Mechanical Properties and Orientation Parameter of Produced Blends.

		LCP content (wt %)	E-modulus (GPa)	σmax (MPa)	S (−)
tape	PLLA	0	3.1 ± 0.26	36 ± 3.3	0
	LCP-A	10	6.1 ± 0.49	58 ± 4.3	>0.8
		30	13.3 ± 0.75	145 ± 10	>0.8
	LCP-B	10	4.8 ± 0.75	61 ± 4.8	>0.8
		30	5.5 ± 0.59	59 ± 8.8	>0.8
injection-molded bar	PLLA	0	3.6 ± 0.22	67 ± 5.1	0
	LCP-A	10	5.4 ± 0.17	100 ± 1.8	0.65
		20	6.5 ± 0.30	127 ± 3.2	0.61
		30	8.0 ± 0.30	138 ± 2.9	0.65
		100	17.0 ± 0.65	251 ± 7.9	0.75
	LCP-B	10	4.2 ± 0.03	77 ± 3.2	0.75
		20	3.7 ± 0.03	73 ± 4.1	0.62
		30	3.9 ± 0.12	68 ± 0.7	0.64
		100	1.5 ± 0.21	35 ± 4.1	0.49