Table 2.

Experimental cutting force components for different cutting regimes and researched materials.

No. v (m/min) s1 (mm/t) a (mm) DI ADI
Fx Fy Fz Fx Fy Fz
1 44 0.178 1 402 150 137 461 242 216
2 71 0.178 1 467 188 160 526 260 224
3 44 0.28 1 582 229 193 710 273 237
4 71 0.28 1 687 286 238 736 310 280
5 44 0.178 1.8 787 324 211 875 351 322
6 71 0.178 1.8 868 398 238 888 431 319
7 44 0.28 1.8 1246 466 345 1271 619 350
8 71 0.28 1.8 1349 565 416 1369 706 400
9 55 0.223 1.51 820 358 284 845 394 296
10 55 0.22 1.5 817 398 282 842 356 328
11 55 0.221 1.5 869 356 260 876 351 287
12 55 0.223 1.5 870 390 261 877 360 290
13 44 0.178 1.07 404 152 139 470 245 219
14 55 0.178 1 443 166 155 486 258 225
15 71 0.179 1 487 192 165 536 270 235
16 44 0.179 1 412 163 127 465 250 221
17 44 0.223 1 527 209 148 599 229 145
18 44 0.281 1 590 243 202 720 284 241
19 44 0.178 1.04 408 155 133 464 247 225
20 44 0.178 1.5 582 229 193 754 327 227
21 44 0.178 1.83 898 331 215 885 358 410