Figure 4.

Mechanical and thermal characterization of B‐a, 2 e, and 1 e formulations. A) Preparation of flexural testing samples by compression molding. B) DSC thermograms revealing curing behavior of monomers B‐a, 2 e and 1 e, ΔT=10 °C min⁻¹ in nitrogen. C) Representative appearance of flexural testing samples. Scale bars correspond to 0.5 cm. D) Representative stress‐strain behavior in flexion of cured thermosets. E) Flexural modulus of cured thermosets (N=8, 9 and 6 for B‐a, 2 e and 1 e, respectively). F) Flexural strength of cured thermosets (N=8, 9 and 6 for B‐a, 2 e and 1 e, respectively). G) Thermal gravimetric analysis of cured thermosets prepared by compression molding (N₂, heating rate of 10 °C min⁻¹).