Table 1. Polymerization Condition at Each Run and the Corresponding Results.

entry	[initiator]a	[monomer]b	solvent	temp (°C)	Dn (μm)	CV (%)	Dz (μm)	yield (%)
1	1%	2%	phenyl acetate	95	0.62	7.5	0.79	12
2	2%	2%	phenyl acetate	95	1.05	6.5	1.13	75
3	3%	2%	phenyl acetate	95	0.92	5.0	1.06	71
4	4%	2%	phenyl acetate	95	0.97	3.7	1.08	73
5	2%	1%	phenyl acetate	95	0.82	5.4	0.84	31
6	2%	3%	phenyl acetate	95	0.95	6.7	1.02	67
7	2%	4%	phenyl acetate	95	1.03	6.8	1.07	70
8	2%	2%	phenyl acetate	65	0.70	5.2	0.88	89
9	2%	2%	ethyl acetate	65	1.44	5.4	1.79	57

^aw/w ratio to monomer.

^bw/v ratio to solvent; D_n = number-average diameter determined via SEM (min. 100 particles); C_v = D_n/SD; D_z = z-average diameter determined via DLS; yield = weight of particles/weight of monomers.