Table 1.

Properties of printed and sintered Fe–6Si including density, shrinkage, grain size, hardness, and carbon content.

Property Result
Theoretical Density of Fe-6.5%Si (g/cm3) 7.48
Green Density (g/cm3, %TD) 4.2, 58 (geometric only)
Final Density (g/cm3, %TD) 7.31, 99 (Archimedes only)
Shrinkage (linear %) 20
Grain size from EBSD after sintering (μm) 56.3 ± 32.8
Grain size after sintering and annealing in H2 (μm) 61.1 ± 35.9
Hardness (GPa) 3.92 ± 0.12
Carbon content of powder (wt.%) 0.010
Carbon content after sintering (wt.%) 0.247