Table 3.
Mechanical tests results (σR is the samples strength, εR the strain at break, E the modulus and ρ the density).
| Formulation | σR (MPa) | εR (mm/mm) | E (MPa) | ρ (g/cm3) |
|---|---|---|---|---|
| Compression Tests | ||||
| OF80_HUF | 1.75 ± 0.36 | 0.16 ± 8.5E-02 | 40.79 ± 3.48 | 0.76 ± 0.02 |
| OF70_LUF | 1.98 ± 0.72 | 0.27 ± 6E-03 | 26.61 ± 6.16 | 0.75 ± 0.04 |
| OF50_MF | 5.17 ± 1.04 | 0.12 ± 1.3E-02 | 86.48 ± 10.69 | 0.86 ± 0.05 |
| Tension Tests | ||||
| OF80_HUF | 0.41 ± 0.13 | 0.07 ± 1.5E-02 | 79.14 ± 46.63 | |
| OF70_LUF | 0.44 ± 0.10 | 0.03 ± 1.4E-02 | 74.07 ± 20.84 | |
| OF50_MF | 1.02 ± 0.12 | 0.02 ± 3E-03 | 126.69 ± 15.87 | |
| Flexural Tests | ||||
| OF80_HUF | 0.76 ± 0.24 | 0.07 ± 0.02 | 75.87 ± 21.51 | |
| OF70_LUF | 1.21 ± 0.17 | 0.01 ± 2E-03 | 118.27 ± 17.10 | |
| OF50_MF | 2.79 ± 0.41 | 0.01 ± 2E-03 | 236.43 ± 41.61 | |