Table 3.
The comparison of textural properties of samples in this work with the literature values.
| Carbon structure | T (°C) | SBET (m2/g) | Vt (cm3/g) | Vmi (cm3/g) | Nco2 (mmol/g) (Condition) | References |
|---|---|---|---|---|---|---|
| Hierarchical porous carbons | 900°C | 936 | 0.553 | 0.32 | 2.84 (25°C 1 bar) |
This work |
| Hierarchical macroporous nitrogen-doped carbons | 600°C | 682.8 | − | − | 2.69 (25°C 1 bar) |
Li et al., 2016 |
| Hierarchical porous graphene-based carbons | 850°C | 459 | 1.17 | 0.11 | 1.76 (0°C 1 bar) |
Xia et al., 2014 |
| Ordered mesoporous carbon | 850°C | 1400 | 1.02 | 0.42 | 2.64 (25°C 1 bar) |
Mahurin et al., 2014 |
| Nitrogen-doped microporous carbons | 800°C | 2567 | 1.49 | 1.25 | 2.78 (25°C 1 bar) |
Fan et al., 2013 |
| Nitrogen-doped mesoporous carbons | 600°C | 537 | 0.47 | 0.17 | 2.8 (25°C 1 bar) |
Wei et al., 2013 |
| Mesoporous carbon | 900°C | 3325 | 2.25 | 0.98 | 2.4 (25°C 1 bar) |
Huang et al., 2016 |
| Mesoporous carbon | 800°C | 974 | 1.93 | 0.1 | 2.41 (25°C 1 bar) |
Lee et al., 2014 |
| Mesoporous carbon | 800°C | 748 | 0.49 | 0.23 | 2.73 (25°C 1 bar) |
Zhang et al., 2015 |