Table 4.
Results from TGA measurements.
| Sample | Additive | PO43− | TPeak | m500°C |
|---|---|---|---|---|
| [wt.%] | [°C] | [wt.%] | ||
| WS-K (C) | - | 38.8 | 202, 263, 493, 649 | 52.2 |
| wood fiber | untreated | 00.0 | 335, 479 | 00.5 |
| KF | 00.7 | 239, 321, 497 | 15.1 | |
| MAP | 08.3 | 140–245(sh), 274, 515 | 26.5 | |
| WS-K (PM) | 03.5 | 187, 246, 488, 698 | 29.0 | |
| WS-K (U) | 04.6 | 130–230(sh), 251, 487, 654 | 32.5 | |
| WS-K (C) | 03.9 | 201, 262, 494, 639 | 31.9 |
Additive content on wood fiber 10 wt.%, TPeak temperature of maximum weight loss rates from DTG curves, m500 °C residual mass at 500 °C, KF commercial flame retardant, sh shoulder.