Table 4.
Chemical compositions of the respective HEA FCC matrix obtained by EDS analysis of materials in as-sintered and annealed conditions.
| Sintered Alloys | Annealed Alloys | |||
|---|---|---|---|---|
| Ti0.3 | Measured Composition [at.%] | Target Composition [at.%] | Measured Composition [at.%] | Target Composition [at.%] |
| Co | 27.97 ± 0.53 | 28.3 | 27.63 ± 0.16 | 28.3 |
| Cr | 17.28 ± 0.44 | 18.87 | 19.33 ± 0.12 | 18.87 |
| Fe | 20.11 ± 0.51 | 18.87 | 21.09 ± 0.16 | 18.87 |
| Ni | 30.05 ± 0.69 | 28.3 | 27.17 ± 0.18 | 28.3 |
| Ti | 4.59 ± 0.83 | 5.66 | 4.79 ± 0.61 | 5.66 |
| Ti0.5 | Measured Composition [at.%] | Target Composition [at.%] | Measured Composition [at.%] | Target Composition [at.%] |
| Co | 27.36 ± 0.70 | 27.27 | 26.60 ± 0.22 | 27.27 |
| Cr | 16.82 ± 0.31 | 18.18 | 18.46 ± 0.10 | 18.18 |
| Fe | 20.60 ± 1.03 | 18.18 | 21.14 ± 0.19 | 18.18 |
| Ni | 28.56 ± 0.34 | 27.27 | 26.23 ± 0.26 | 27.27 |
| Ti | 6.66 ± 1.81 | 9.09 | 7.58 ± 0.76 | 9.09 |
| Ti0.7 | Measured Composition [at.%] | Target Composition [at.%] | Measured Composition [at.%] | Target Composition [at.%] |
| Co | 25.90 ± 0.54 | 26.32 | 25.57 ±0.47 | 26.32 |
| Cr | 16.95 ± 0.94 | 17.54 | 17.90 ± 0.19 | 17.54 |
| Fe | 19.45 ± 1.04 | 17.54 | 19.76 ± 0.26 | 17.54 |
| Ni | 27.82 ± 1.78 | 26.32 | 25.17 ± 0.77 | 26.32 |
| Ti | 9.88 ± 1.42 | 12.28 | 11.60 ± 1.50 | 12.28 |