. 2020 Feb 4;13(3):689. doi: 10.3390/ma13030689

Table 8.

Test results of resistance to molten iron splash according to the modified test method: the angle of iron outpour onto the sample was 60° and the time of metal outpour onto the sample was 7.5 s.

#	Material	Protective Parameter		Change in Sample Thickness X, mm	Mean of X, mm (SD)
#	Material	Mass of Metal Poured, g	Molten Metal Splash Index	Change in Sample Thickness X, mm	Mean of X, mm (SD)
1	ASP	300 300 300	300	20 17 18	18 (2)
2	AP	300 300 300	The damage of PVC film	-	-

SD—standard deviation. Note: For protective parameters (“mass of metal poured” and “molten metal splash index”), the mean and standard deviation (SD) were not calculated, because these parameters were obtained by trial-and-error by repeating the procedure of pouring a smaller or larger amount of metal, until the minimum amount of metal that initiated PVC (polyvinyl chloride) film damage was determined.