. 2020 Feb 21;25(4):974. doi: 10.3390/molecules25040974

Table 1.

Some physical data of E-Pn PMONPs and P3 PMONPs.

Material	N₂-Sorption Measurements			Particles Size (nm) ^c	Zêta Potential		TGA ^d
Material	S_BET (m²·g⁻¹)	V_pore (cm³·g⁻¹) ^a	∅_pore (nm) ^b	Particles Size (nm) ^c	pH	(mV)	TGA ^d
E-P1 90/10 PMONPs	683	0.48	2.8	447	6.96	−28	78%
E-P2 90/10 PMONPs	509	0.34	2.7	800	5.92	32	75%
E-P3 90/10 PMONPs	505	0.36	2.8	479	5.44	36	72%
E-P1 75/25 PMONPs	low	nd	nd	507	7.34	−22	67%
E-P2 75/25 PMONPs	low	nd	nd	513	6.25	20	58%
E-P3 75/25 PMONPs	low	nd	nd	321	4.86	24	57%
P3 PMONPs	186	0.26	5.6	269	8.94	11	nd ^e

^a Determined from the uptake at saturation at p/p° = 0.98. ^b Diameter determined by BJH. ^c Hydrodynamic diameters from DLS. ^d Residual mass, TGA with a heating rate of 10 °C/min from 30 to 1000 °C. ^e Not determined.