Published in final edited form as: Microporous Mesoporous Mater. 2020 Jul 14;308:110454. doi: 10.1016/j.micromeso.2020.110454

Table 2.

Textural parameters of MBGs as powders and after being processed into disks (SBET: BET surface area, VP: pore volume and DP pore diameter). MBGs composition (atom-%) determined by EDS is also included. Standard deviations were omitted for simplifcation, but they were for all the values inferior to 7%.

Sample Powders Disks Composition (atomic-%)
SBET(m2g−1) Vp (cm3g−1) DP (nm) SBET(m2g−1) Vp (cm3g−1) DP (nm) Si P Ca Cu
0% Cu_HNO 3 301 0.41 6.7 261 0.35 6.7 89.6 2.2 8.2 0
2.5% Cu_HNO 3 275 0.38 6.2 228 0.31 6.2 85.8 4.4 7.2 2.7
5% Cu_HNO 3 261 0.35 6.1 216 0.28 6.2 82.3 2.4 8.3 5.3
0% Cu_HCl 218 0.40 8.8 211 0.38 8.8 85.4 7.1 7.5 0
2.5% Cu_HCl 295 0.46 8.4 288 0.44 8.8 80.6 10.2 7.6 1.6
5% Cu_HCl 290 0.47 8.8 282 0.45 8.9 80.7 8.4 8.6 2.4