Published in final edited form as: Biomaterials. 2019 Dec 26;235:119728. doi: 10.1016/j.biomaterials.2019.119728

Table 3.

Characteristics of selected star-like polymers with comparable molar masses

Sample Core/Pola) [kg mol−1] b) Ð Generation of core Molar ratio Pol : core No. of chains on core Dh (int.) c) [nm]
S10 Dendron/P1-TT 149 1.01 G4 16 : 1 7.8 16.3±0.2
S28 Dendron/P2-TT 156 1.06 G3 4 : 1 3.7 18.5 ±0.4
S22 Dendrimer/P1-Prg 150 1.06 G4 8 : 1 7.7 17.1±1.0
S37 Dendrimer/P2-Prg 166 1.12 G2 4 : 1 3.9 19.8±0.6
a)

Type of dendritic core used (Dendron = bisMPA dendron, dendrimer = bisMPA dendrimer,), Pol = polymer precursor used for star-like polymer formulation

b)

Molecular weights and dispersity were determined by SEC using multi-angle light scattering and refractive index detectors.

c)

Hydrodynamic diameter was measured by DLS in 0.15M NaCl