Table 6.
Summary of the tensile testing results.
| Specimen Composition | Mechanical Properties | Mean | SD |
|---|---|---|---|
| PLA/PCL | Elongation at Break (%) | 5.77 | 0.88 |
| Ultimate Stress (MPa) | 62.97 | 4.31 | |
| Modulus of Elasticity (GPa) | 1.08 | 0.07 | |
| PLA/PCL/5HA | Elongation at Break (%) | 6.05 | 1.39 |
| Ultimate Stress (MPa) | 57.47 | 2.01 | |
| Modulus of Elasticity (GPa) | 0.92 | 0.18 | |
| PLA/PCL/15HA | Elongation at Break (%) | 5.61 | 0.39 |
| Ultimate Stress (MPa) | 52.05 *,# | 2.44 | |
| Modulus of Elasticity (GPa) | 0.98 | 0.10 |
* Statistically significant vs. PLA/PCL, # Statistically significant vs. PLA/PCL/5HA.