Table 8.
Mechanical properties of the materials.
| Materials | Compressive Strength (MPa) | Tensile Strength (MPa) | Bending Strength (MPa) |
|---|---|---|---|
| Previous Studies | |||
| Polylactic acid: PLA | 18–93 [64] | 46–66 [64] | 97 [65] |
| Polycaprolactone: PCL | 11.9–15.9 [66,67] | 16 [68] | 29 [65] |
| Hydroxyapatite: HA | 174 [69] | 50 [70] | - |
| Cortical bone | 90–200 [71] | 52 [70] | 51 [70] |
| Cancellose bone | 7–16 [72,73] | 7.4 [70] | - |
| PLA filament | - | 59.51 [40] | - |
| PLA 3D-Printed | 85.72 ± 4.43 [42] | 65.49 [40] | 102.20 [40] |
| PLA/5HA 3D-Printed | 86.03 ± 7.00 [42] | - | - |
| PLA/15HA 3D-Printed | 85.66 ± 5.77 [42] | - | - |
| PLA/PCL/TiO2 3D-Printed | - | 45 [60] | - |
| Current Study | |||
| PLA/PCL filament | - | 51.27 ± 1.51 | - |
| PLA/PCL/5HA filament | - | 49.02 ± 2.13 | - |
| PLA/PCL/15HA filament | - | 45.73 ± 1.15 | - |
| PLA/PCL 3D-Printed | 76.85 ± 3.16 | 62.97 ± 4.31 | 103.44 ± 2.23 |
| PLA/PCL/5HA 3D-Printed | 81.14 ± 2.64 | 57.47 ± 2.01 | 101.21 ± 7.73 |
| PLA/PCL/15HA 3D-Printed | 82.72 ± 1.76 | 52.05 ± 2.44 | 101.10 ± 4.97 |