Table 2.
Self-healing efficiencies and mechanical properties of FEEMA64_mGO series before and after the healing test.
| Sample | Before Healing Test | After Healing Test | Self-Healing Efficiency 1 (%) | ||
|---|---|---|---|---|---|
| Tensile Strength (MPa) | Elongation at Break (%) | Tensile Strength (MPa) | Elongation at Break (%) | ||
| FEEMA64 polymer film | 2.648 ± 0.257 | 214.667 ± 14.687 | 1.663 ± 0.261 | 12.600 ± 0.898 | 5.724 |
| FEEMA64_mGO0.015 wt% | 4.021 ± 0.229 | 198.235 ± 10.232 | 3.611 ± 0.155 | 36.465 ± 12.070 | 23.560 |
| FEEMA64_mGO0.030 wt% | 4.566 ± 0.564 | 69.035 ± 9.383 | 2.916 ± 0.171 | 61.465 ± 1.322 | 81.228 |
| FEEMA64_mGO0.050 wt% | 4.022 ± 0.542 | 155.510 ± 6.980 | 2.927 ± 0.151 | 141.333 ± 7.588 | 82.033 |
1 Healing efficiency calculated using elongation at break.