Table 1.
Properties of TOPAS® 5013-10L COC.
| Terms | Value | Test Method |
|---|---|---|
| Melt Mass Flow Rate/(g/10min) | 48.96 | ISO 1133 |
| Solid density/(g/cm3) | 1.02 | ISO 1183 |
| Number-average Molecular Weight/(—) | 83198 | GPC |
| Polymer dispersity index/(—) | 1.56104 | |
| Water absorption rate/(%) | 0.01 | ISO 62 |
| Moisture Permeability Coefficient/(g.mm/m2.d) | 0.03 | DIN 53 122 |
| Elastic Modulus/(MPa) | 3200 | ISO 527-2/1A |
| Tensile strength/(MPa) | 46 | |
| Elongation at Break/(%) | 1.70 | |
| Glass Transition Temperature/(°C) | 134 | DSC |
| Heat Deflection Temperature/(°C) | 127 (0.45 MPa) | ISO75 part1 and part2 |
| Transmittance/(%) | 91 (t = 2 mm) | ISO 13468-2 |
| Index of Refraction/(—) | 1.53 | ISO 13468-2 |