Table 3.

The curing kinetic parameters of the samples based on Friedman and Kissinger models.

Designation	β (°C/min)	Ēa (kJ/mol)	ln A (s−1)	Mean (s−1)	m	Mean	n	Mean
Friedman
Epoxy	5	72.5	22.2	22.0	0.40	0.39	1.17	0.94
	10		22.1		0.39		1.00
	15		21.9		0.41		0.83
	20		21.9		0.37		0.78
E-0.1AHP	5	64.4	19.6	19.3	0.27	0.29	1.12	0.89
	10		19.3		0.31		0.91
	15		19.2		0.31		0.77
	20		19.2		0.26		0.74
E-0.3AHP	5	77.2	23.4	23.3	0.53	0.49	1.03	0.93
	10		23.4		0.51		0.94
	15		23.3		0.47		0.90
	20		23.3		0.44		0.85
E-0.5AHP	5	80.7	24.6	24.5	0.56	0.52	1.19	1.06
	10		24.6		0.54		1.09
	15		24.5		0.53		0.98
	20		24.5		0.46		0.97
Kissinger
Epoxy	5	62.4	18.9	18.8	0.26	0.25	1.08	0.87
	10		18.9		0.25		0.92
	15		18.7		0.27		0.77
	20		18.8		0.24		0.71
E-0.1AHP	5	54.9	16.5	16.4	0.14	0.16	1.04	0.82
	10		16.4		0.18		0.83
	15		16.3		0.18		0.71
	20		16.4		0.13		0.69
E-0.3AHP	5	69.3	21.0	21.0	0.43	0.39	0.97	0.88
	10		21.0		0.41		0.89
	15		21.1		0.371		0.85
	20		21.0		0.34		0.80
E-0.5AHP	5	72.5	21.9	21.9	0.44	0.41	1.11	0.99
	10		21.9		0.42		1.03
	15		21.9		0.41		0.92
	20		22.0		0.34		0.91