Table A1.
Experimental Number | Run Order | Mould Temperatures (°C) | Injection Speeds (mm/s) | Back-Pressure (MPa) | Melt Temperature (°C) | Holding Time (s) |
---|---|---|---|---|---|---|
30 | 1 | 90.0 | 100.0 | 16.0 | 260.0 | 7.0 |
32 | 2 | 90.0 | 267.8 | 16.0 | 260.0 | 7.0 |
18 | 3 | 90.0 | 100.0 | 12.0 | 155.0 | 7.0 |
10 | 4 | 90.0 | 100.0 | 12.0 | 260.0 | 0.0 |
22 | 5 | 90.0 | 100.0 | 16.0 | 155.0 | 7.0 |
2 | 6 | 90.0 | 100.0 | 12.0 | 155.0 | 0.0 |
13 | 7 | 25.0 | 100.0 | 16.0 | 260.0 | 0.0 |
14 | 8 | 90.0 | 100.0 | 16.0 | 260.0 | 0.0 |
24 | 9 | 90.0 | 267.8 | 16.0 | 155.0 | 7.0 |
28 | 10 | 90.0 | 267.8 | 12.0 | 260.0 | 7.0 |
11 | 11 | 25.0 | 267.8 | 12.0 | 260.0 | 0.0 |
4 | 12 | 90.0 | 267.8 | 12.0 | 155.0 | 0.0 |
12 | 13 | 90.0 | 267.8 | 12.0 | 260.0 | 0.0 |
8 | 14 | 90.0 | 267.8 | 16.0 | 155.0 | 0.0 |
27 | 15 | 25.0 | 267.8 | 12.0 | 260.0 | 7.0 |
15 | 16 | 25.0 | 267.8 | 16.0 | 260.0 | 0.0 |
20 | 17 | 90.0 | 267.8 | 12.0 | 155.0 | 7.0 |
29 | 18 | 25.0 | 100.0 | 16.0 | 260.0 | 7.0 |
26 | 19 | 90.0 | 100.0 | 12.0 | 260.0 | 7.0 |
33 | 20 | 57.5 | 183.9 | 14.0 | 207.5 | 3.5 |
31 | 21 | 25.0 | 267.8 | 16.0 | 260.0 | 7.0 |
17 | 22 | 25.0 | 100.0 | 12.0 | 155.0 | 7.0 |
1 | 23 | 25.0 | 100.0 | 12.0 | 155.0 | 0.0 |
25 | 24 | 25.0 | 100.0 | 12.0 | 260.0 | 7.0 |
23 | 25 | 25.0 | 267.8 | 16.0 | 155.0 | 7.0 |
3 | 26 | 25.0 | 267.8 | 12.0 | 155.0 | 0.0 |
6 | 27 | 90.0 | 100.0 | 16.0 | 155.0 | 0.0 |
16 | 28 | 90.0 | 267.8 | 16.0 | 260.0 | 0.0 |
19 | 29 | 25.0 | 267.8 | 12.0 | 155.0 | 7.0 |
9 | 30 | 25.0 | 100.0 | 12.0 | 260.0 | 0.0 |
5 | 31 | 25.0 | 100.0 | 16.0 | 155.0 | 0.0 |
21 | 32 | 25.0 | 100.0 | 16.0 | 155.0 | 7.0 |
7 | 33 | 25.0 | 267.8 | 16.0 | 155.0 | 0.0 |