Table 2. Thermodynamic Data Obtained by High-Temperature Drop Combustion Calorimetry Measurements at 800 °C in O2.
| compound | formula | ΔHcom (kJ/mol formula) | ΔHr° (kJ/mol of M) | H800° – H25° (kJ/mol) |
|---|---|---|---|---|
| Mg-MOF-74 | Mg2[C8H2O6] | –3079.9 ± 16.44 | 303.89 ± 17.21 | |
| Ni-MOF-74 | Ni2[C8H2O6] | –2989.9 ± 18.76 | 264.38 ± 19.44 | |
| H4DOBDC | C8H6O6 | –2394.0 ± 5.12 | ||
| MgO | MgO | 34.24 | ||
| NiO | NiO | 39.73 | ||
| H2O | H2O | 73.30 | ||
| ZIF-1 | C6H6N4Zn | 19.9 ± 2.537 | ||
| ZIF-4 | C6H6N4Zn | 22.1 ± 2.737 | ||
| ZIF-7 | C14H10N4O2.24Zn | 27.2 ± 3.937 | ||
| ZIF-8 | C8H10N4Zn | 27.1 ± 1.937 | ||
| qtz-Zn(CF3Im)2 | C7H6N4F3Zn | 27.1 ± 1.041 | ||
| SOD-Zn(CF3Im)2 | C7H6N4F3Zn | 42.7 ± 1.141 |