Table 1.
Structural characterization data of P(St-ran-MA) copolymers.
| Sample Name | St:MAc | Mn (kDa)c | Mn (kDa)d | PDId | ε245e |
|---|---|---|---|---|---|
| P(St31-ran-MA31)a | 1.00/1.00 | 6.6 | 6.7 | 1.05 | 12.8 |
| P(St18-ran-MA9)a | 2.00/1.00 | 3.1 | 3.1 | 1.05 | 17.2 |
| P(St40-ran-MA21)a | 1.93/1.00 | 6.6 | 6.4 | 1.04 | 17.7 |
| P(St76-ran-MA39)a | 1.95/1.00 | 12.6 | 12.0 | 1.13 | 18.0 |
| P(St-ran-MA)b | 0.95/1.00 | / | 4.6 | 1.22 | / |
| P(St-ran-MA)b | 2.00/1.00 | / | 5.0 | 1.52 | / |
| P(St-ran-MA)b | 2.86/1.00 | / | 5.7 | 1.59 | / |
aSynthesized via RAFT polymerization; bLipodisq copolymers obtained from Malvern Cosmeceutics; cObtained by NMR analysis; dObtained by GPC analysis; eThe ε245 of polystyrene (PSt62) was 25.6 mM−1 cm−1 (see Supplementary Fig. 2).