Table 10. Mean values of Δ_topol and Δ_cryst for polyhedra distorted as a result of the pseudo-JTE.

	No. of coordination polyhedra	〈Δtopol〉	〈Δcryst〉	Maximum Δcryst	Compound, ICSD refcode and reference
[4]	36 (8 ions)	0.11	0.092	0.217	KCu2+ 5V5+ 3O13 (400802; Martin & Müller-Buschbaum, 1994a ▸)
[5]	14 (7 ions)	0.173	0.159	0.256	Cs[Mo6+ 2O3(PO4)2] (79517; Hoareau et al., 1995 ▸)
[6]	67 (12 ions)	0.144	0.181	0.531	K2Mo6+O2(I5+O3)4 (170119; Ok & Halasyamani 2005a ▸)
[7]	6 (3 ions)	0.06	0.115	0.192	La(Nb5+ 5O14) (33783; Hofmann & Gruehn, 1990 ▸)
[8]	7 (4 ions)	0.06	0.087	0.131	KY(W6+O4) (411285; Gallucci et al., 2000 ▸)
[9]	1	0.078	0.11	0.11	Y3Re7+O8 (15505; Baud et al., 1981 ▸)
[10]	1	0.086	0.079	0.079	YCo2+(BO2)5 (20670; Abdullaev et al., 1980 ▸)
[5]Cr2+	2	0.039	0.077	0.077	SrCr2+(P2O7) (280309; Maaß & Glaum, 2000 ▸)
[5]Co2+	1	0.032	0.07	0.07	BaCo2+ 2(Si2O7) (81473; Adams et al., 1996 ▸)
[5]Cu2+	13	0.061	0.084	0.133	Cu2+ 4O(PO4)2 (50459; Schwunck et al., 1998 ▸)
[6]Zn2+	5	0.056	0.050	0.129	Mn2+Zn2Ta5+ 2O8 (85042; Rohweder & Müller-Buschbaum, 1989 ▸)
[6]Hg2+	2	0.032	0.038	0.066	Hg2+(PO3)2 (280292; Weil & Glaum, 2000 ▸)