Table 1. Thermal, Optical, and Photophysical Properties of the Synthesized Materials.

ID	Tg [°C]a	Tdec [°C]a	λabs [nm]b	λem [nm]b	IP [eV]c	Eg [eV]d	μ0 [cm2 V–1 s–1]e
V1209	187	432	238, 293, 308	459	4.93	2.78	3.5 × 10–5
V1221	184	436	238, 294, 308	459	4.83	2.76	3 × 10–6
V1225	192	441	238, 292, 309	459	4.91	2.78	3 × 10–5
V1207	154	385	239, 292, 310	459	4.82	2.79	5 × 10–5

^aGlass transition (T_g) and decomposition (T_dec) temperatures observed from DSC and TGA, respectively (10 °C/min, N₂ atmosphere).

^bAbsorption and emission (excitation = λ_{abs max}) spectra measured in THF solution (10^–4 M).

^cIonization energies of the films measured using PESA.

^dE_g estimated from the intersection of absorption and emission spectra.

^eMobility value at zero field strength.