Table 4.
Mechanical properties of different epoxy/poly(ether imide) (PEI) systems investigated in literature at room temperature.
| Sample | Molecular Weight of PEI, Mn (g/mol) | Tensile Strength (MPa) | Tensile Modulus (GPa) | Elongation at Break (%) | KIC (MPa·m1/2) | GIC (kJ/m2) | Ref. |
|---|---|---|---|---|---|---|---|
| BADCy | 63.7 | 2.27 | 4.14 | 0.62 | 0.100 | [33] | |
| BADCy/PEI = 90/10 | 12,000 | 75.6 | 2.38 | 4.66 | 1.35 | 0.495 | [33] |
| BADCy/PEI = 85/15 | 12,000 | 84.7 | 2.39 | 5.86 | 1.6 | 0.680 | [33] |
| BADCy/PEI = 80/20 | 12,000 | 73.4 | 2.00 | 5.50 | 3.1 | 2.480 | [33] |
| BADCy | 84.2 | 2.60 | 4.43 | - | 0.190 | [82] | |
| BADCy/PEI = 95/5 | 18,000 | 82.1 | 2.57 | 4.33 | - | 0.211 | [82] |
| BADCy/PEI = 90/10 | 18,000 | 83.4 | 2.54 | 4.50 | - | 0.202 | [82] |
| BADCy/PEI = 85/15 | 18,000 | 99.2 | 2.53 | 6.20 | - | 0.603 | [82] |
| BADCy/PEI = 80/20 | 18,000 | 108.4 | 2.54 | 7.33 | - | 1.207 | [82] |
| BADCy/PEI = 75/25 | 18,000 | 110.9 | 2.55 | 7.91 | - | 2.105 | [82] |
| HPT | - | - | - | 0.60 | - | [78] | |
| HPT/PEI = 95/5 | 20,000 | - | - | - | 1.18 | - | [78] |
| HPT/PEI = 90/10 | 20,000 | - | - | - | 1.22 | - | [78] |
| HPT/PEI = 85/15 | 20,000 | - | - | - | 1.35 | - | [78] |
| BADCy | - | - | - | - | 0.196 | [32] | |
| BADCy/PEI = 92.5/7.5 | 18,000 | - | - | - | - | 0.261 | [32] |
| DGEBA/PEI = 87/13 | 19,000 | 49.3 | 0.67 | 7.1 | - | - | [83] |
| TGDDM + DGEAC | 62.0 | 2.6 | 3.2 | - | - | [84] | |
| TGDDM + DGEAC/PEI = 85/15 | 23,825 | 80.9 | 2.6 | 3.5 | - | - | [84] |
| TGDDM + DGEAC/PEI = 80/20 | 23,825 | 88.8 | 2.6 | 4.7 | - | - | [84] |
| TGDDM + DGEAC/PEI = 85/15 | 25,405 | 87.3 | 2.7 | 4.3 | - | - | [84] |
| TGDDM + DGEAC/PEI = 80/20 | 25,405 | 88.8 | 2.6 | 4.7 | - | - | [84] |
| TGDDM + DGEAC/PEI = 85/15 | 21,175 | 77.0 | 2.6 | 3.9 | - | - | [84] |
| TGDDM + DGEAC/PEI = 80/20 | 21,175 | 81.6 | 2.6 | 4.2 | - | - | [84] |
| TGDDM + DGEAC/PEI = 85/15 | 20,983 | 89.2 | 2.7 | 4.4 | - | - | [84] |
| TGDDM + DGEAC/PEI = 80/20 | 20,983 | 86.6 | 2.7 | 4.4 | - | - | [84] |