. 2020 Oct 10;10(10):1998. doi: 10.3390/nano10101998

Figure 8.

Figure 8

(a) Direct comparison of the simulation results of 270-nm period nanostructuring at a high incident fluence of 485 mJ/cm2 with (b) the experimental data obtained for 470 mJ/cm2. (c) Direct comparison of the simulation results of 500-nm period nanostructuring at a high incident fluence of 485 mJ/cm2 with (d) the experimental data obtained for 500 mJ/cm2. The atoms are colored by local order parameter (LOP) used here for identification of the extremely fast melting process. The liquid phase is characterized by a rapid jump of LOP above cut-off value 0.5.