. 2020 Oct 13;12(10):2343. doi: 10.3390/polym12102343

Table 7.

Viscoelasticity properties per one phr of filler by different cure temperatures.

Cure Temperature		150 °C	160 °C	170 °C	RoC
Tan ẟ at 60 °C per CBBR or SSRN (10⁴ g∙phr/mol)	Carbon black variate (CBBR)	1439.7	1468	1628.9	9.46
Tan ẟ at 60 °C per CBBR or SSRN (10⁴ g∙phr/mol)	Silica variate (SSRN)	439.14	411.29	442.43	0.165
G″ at 0 °C per CBBR or SSRN (10¹¹ MPa·g∙phr/mol)	Carbon black variate (CBBR)	1.676	1.732	1.971	0.015
G″ at 0 °C per CBBR or SSRN (10¹¹ MPa·g∙phr/mol)	Silica variate (SSRN)	2.213	2.071	2.041	-0.008
G* at −20 °C per CBBR or SSRN (10¹¹ MPa·g∙phr/mol)	Carbon black variate (CBBR)	1.626	1.667	1.917	0.145
G* at −20 °C per CBBR or SSRN (10¹¹ MPa·g∙phr/mol)	Silica variate (SSRN)	2.135	1.970	1.951	−0.092