Table 3.

Summary of the tensile properties of Al-12Si alloy.

Composition	Process	Condition	Yield Strength (MPa)	Ultimate Strength (MPa)	Strain at Facture (%)	Reference
Al-12Si	Casting	As-prepared	145	300	2.5	[196]
Al-12Si	Cast	As-prepared	65	200	9.5	[67]
Al-12Si	SLM	N2 atmosphere	224 ± 7	368 ± 11	4.8 ± 0.6	[197]
Al-12Si	SLM	Ar atmosphere	223 ± 11	355 ± 8	4.2 ± 0.6	[197]
Al-12Si	SLM	He atmosphere	221 ± 11	342 ± 43	1.5 ± 0.6	[197]
Al-12Si	SLM	As-prepared	260	385	3	[67]
Al-12Si	SLM	As-prepared	225	350	5	[130]
Al-12Si	SLM	As-prepared	184 ± 9	231 ± 5	1 ± 01	[135]
Al-12Si	SLM	As-prepared	221 ± 10	420 ± 10	4 ± 0.3	[135]
Al-12Si	SLM	As-prepared	154 ± 5	190 ± 3	1 ± 0.1	[135]
Al-12Si	SLM	As-prepared	221 ± 10	419 ± 10	4 ± 0.3	[135]
Al-12Si	SLM	Post-build stress relief—513 K	180 ± 7	220 ± 6	1 ± 0.1	[135]
Al-12Si	SLM	Post-build stress relief—513 K	187 ± 3	230 ± 4	1 ± 0.1	[135]
Al-12Si	SLM	Post-build stress relief—513 K	218 ± 7	372 ± 7	3 ± 0.3	[135]
Al-12Si	SLM	Heat treated—473 K	262	340	2.5	[67]
Al-12Si	SLM	Heat treated—523 K	180	275	5	[67]
Al-12Si	SLM	Heat treated—623 K	120	200	10	[67]
Al-12Si	SLM	Heat treated—673 K	100	160	15	[67]
Al-12Si	SLM	Heat treated—723 K	95	150	13	[67]
Al-12Si	SLM	Solution heat treated (30 min)	110	190	25	[130]