Table 4.
Summary of the tensile properties of AlSi10Mg samples.
| Process | Condition | Yield Strength (MPa) | Ultimate Strength (MPa) | Strain at Fracture (%) | Reference |
|---|---|---|---|---|---|
| Wrought | As-prepared (longitudinal) | 293 | 310 | 15 | [201] |
| Cast | Aged | - | 300–371 | 2.5–3.5 | [197] |
| HDPC * | As-prepared | - | 300–350 | 2.5–3.5 | [197] |
| HDPC * | T6 | - | 330–365 | 3–5 | [199] |
| SLM | As-prepared | 208 | 368 | 4 | [66] |
| SLM | As-prepared hotizontal | 227 | 358 | 4 | [201] |
| SLM | As-prepared vertical | 172 | 289 | 3 | [203] |
| SLM | Building angle—0° | - | 420 | - | [202] |
| SLM | Building angle—45° | - | 405 | - | [202] |
| SLM | Building angle—90° | - | 360 | - | [204] |
| SLM | Horizontal | 250 | 330 | 1 | [163] |
| SLM | Vertical | 240 | 320 | 1 | [163] |
| SLM | XY | - | 391 ± 8 | 5.5 ± 0.4 | [163] |
| SLM | Z | - | 396 ± 8 | 3 ± 1 | [163] |
| SLM | As-prepared | 240 | 360 | 3 | [163] |
| SLM | As-prepared | 268 ± 2 | 333 ± 2 | 1.4 ± 0.3 | [166] |
| SLM | As-prepared | 332 ± 8 | 434 ± 11 | 5.3 ± 0.2 | [160] |
| SLM | T4 | 119 | 212 | 12 | [163] |
| SLM | T6 | 210 | 269 | 10 | [66] |
| SLM | Solutionized | 196 ± 4 | 282 ± 4 | 13.5 ± 0.5 | [156] |
| SLM | T6 | 187 ± 3 | 197 ± 4 | 20 ± 1 | [163] |
| SLM | T6 | 239 ± 2 | 292 ± 4 | 4 ± 1 | [169] |
* High pressure die casting.