Table 13.
Mechanical properties of PLA composites reinforced with jute fibers.
| Fiber Content wt (%) | Process | Tensile Strength (MPa) |
Flexural Strength (MPa) |
Impact Strength (kJ/m2) |
Young’s Modulus (GPa) |
Additional Information | Ref. |
|---|---|---|---|---|---|---|---|
| 50 | IM | 62.2 | 98.8 | 2.21 | - | - | [76] |
| - | IM | 90.7 | - | 4.22 (kJ/m) | 12.3 | Short Fiber Pellet mix | [77] |
| - | CM | 32.3 | 41.8 | 3.5 J | 2.11 | Woven Jute Fabric | [72] |
| 30 | IM | 71.7 | - | - | 9.15 | Lignin 4% | [95] |
| - | RFM | 53.16 | 128.3 | - | 8.11 | - | [75] |
| 20 | IM | 55 | 110 | 1.6 | 1.7 | 10% NaOH + H2O2 | [99,100] |
| 25 | IM | 54 | 80 | 2.5 | 2.7 | 05% NaOH + H2O2 | [99,100] |
| 30 | IM | 70 | - | 26 (J/m) | - | Alkali Treated | [101] |
| 30 | IM | 80 | - | 28(J/m) | - | Alkali + Silane Treated | [101] |
| 15 | IM | 50 | 78 | 4.8 | 4.8 | Treated with DOPO-ICN | [78] |
| 10 | - | 61.71 | 93.68 | 19.26 | 4.2 | Graphene Modified with DOPO | [102] |
| 5 | SC | 70.30 | - | - | 3.30 | PLA Composite Films with Jute Nano Fibers | [103] |
| 3 | SC | 69.80 | - | - | 3.20 | NaOH Treated Jute Nano Fibers | [104] |
| 40 | HP | 77.5 | 115.3 | 3.67 | Core Shell Nanoparticles (SiO2–PBA–NH2) | [105] |
CM—Compression Molding; DOPO—9,10-dihydro-9-oxa-phosphaphenanthrene-10-Oxide; DOPO—ICN-Phosphorus Based Compound; HP—Hot Pressing; IM—Injection Molding; RFM—Resign Film Method; SC—Solvent Casting.