Table 4. Shear bond strength values of glaze-on technique on zirconia for bonding to resin cement.
| Author (Year) | Glaze | Ceramic Substrate | Resin Cement | Bond Strength (MPa) |
|---|---|---|---|---|
| Cheung (2014) | Pre-fired overglaze (Cercon Ceram Kiss) | Zirconia (Cercon) | Panavia F 2.0 | 17.3 ± 1.7 |
| Paste liner | 18 ± 2.6 | |||
| Sandblasting | 3.9 ± 0.7 | |||
| Vanderlei (2014) | Vita Glaze Spray with 9% HF acid | Zirconia (VITA InCeram) | Panavia F 2.0 | 13.3 ± 4.1 |
| Vita Akzent with 9% HF | 9.3 ± 2.7 | |||
| Without surface conditioning | 0.01 ± 0.0 | |||
| Ntala (2010) | Experimental 10 wt% of Hydroxyapatite | Zirconia (Kavo) | Variolink II | 5.6 ± 1.7 |
| 20 wt% Empress glass-ceramic/glaze | 11 ± 3 | |||
| Everson (2011) | Vitadur Alpha with 10% HF | Zirconia (3 M Lava) | Z100 resin based composites | ~ 25 |
| Emax Ceram | ~ 22 | |||
| Noritake Cerabien | ~ 28 | |||
| Vita VM9 | ~ 18 | |||
| Lava Ceram | ~ 20 | |||
| Cura (2012) | ICE Glaze with silane | Zirconia (ICE Zirkon Zahn) | Variolink II | 9 ± 1.3 |
| ICE Glaze with silane | Zirconia primer | 4.9 ± 1.1 | ||
| Valentino (2012) | Cercon Ceram Kiss glaze with silane | Zirconia (Cercon) | Enforce | 25.7 ± 8.7 (Microshear) |
| Cattel (2009) | Experimental alumina-silicate glass powder | Leucite Glass Ceramic | Marathon-v | 9.8 ± 1.9 |
| Present study | Vita Akzent with 5% HF | Zirconia (Katana) | Paracore | 4.4 ± 1.1 |
| Mica-based glaze with 5% HF | 2.8 ± 0.81 | |||
| Sandblasted | 1.3 ± 0.75 |
*
HF is hydrofluoric acid and ~ SD was not placed due to the graphical representation.