Table 3.

Properties of diamonds irradiated with pions and the fluence they received. The initial unirradiated Charge Collection Distance ($\mathit{ccd}$) values for the scCVD diamond sample are given separately for positive and negative bias polarity at 1 V/$\mathsf{\mu }\mathrm{m}$, since the detector collects all the charge at a bias voltage of 200 V. For Samples 6 and 7, only one bias polarity was measured for the unirradiated samples. For these samples, the initial $\mathit{ccd}$ values are listed for comparison but were not used in the analysis.

Diamond	Type	Thickness ($\mathsf{\mu }\mathbf{m}$)	Area (mm${}^2$)	Initial ccd ($\mathsf{\mu }\mathbf{m}$)	Fluence (10${}^{15}$ $\mathbf{\pi }$/cm${}^2$)
Sample 5	scCVD	497	5 × 5	497/497	0
					0.65 ± 0.14
Sample 6	pCVD	520	5 × 5	222	0
					0.32 ± 0.07
Sample 7	pCVD	508	5 × 5	228	0
					0.61 ± 0.14